Mössbauer study of new vanadate glass with large charge-discharge capacity

Charge-discharge capacity and cyclicity of lithium ion battery (LIB) was evaluated in which 15Li₂O·10Fe₂O₃·xSnO₂·5P₂O₅·(70–x)V₂O₅ glass (x?=?0 and 20 in mol%, abbreviated as xLFSPV) was used as a cathode. A local structure of xLFSPV glass before and after charging was investigated by ⁵⁷Fe- and ¹¹⁹Sn-Mössbauer spectroscopies. ⁵⁷Fe-Mössbauer spectrum of xLFSPV glass with ‘x’ of 20 was composed of a doublet with isomer shift (δ) of 0.35_±0.02 mm s^???1 and quadrupole splitting (Δ) of 0.88_±0.03 mm s^???1 due to distorted Fe^IIIO₄ tetrahedra. ¹¹⁹Sn-Mössbauer spectrum of this glass consisted of a doublet with δ of 0.08_±0.01 and Δ of 0.52_±0.01 mms^???1 due to distorted Sn^VIO₆ octahedra. After discharging the battery from 4.5 to 1.0 V, larger δ of 0.40_±0.03 mm s^???1 and Δ of 0.94_±0.04 mm s^???1 were obtained, indicating that both iconicity of Fe-O bonds and local distortion of Fe^IIIO₄ tetrahedra were increased. On the contrary, identical δ of 0.09_±0.01 mm s^???1 and Δ of 0.50_±0.01 mm s^???1 were observed in the ¹¹⁹Sn-Mössbauer spectrum of 20LFSPV glass after the discharge, indicating that chemical environment of Sn^IVO₆ octahedra was not affected after the discharge. Charge-discharge curve of LIB containing 20LFSPV glass as a cathode active material recorded under the current density of 8.3 mA g^???1 (0.011 mA cm^???2) between 1.0 and 4.5 V showed a large initial charge capacity of 431.1 mAh g^???1 and discharge capacity of 382.3 mAh g^???1, respectively. These results indicate that 20LFSPV glass could be a new cathode active material for LIB.     

Mechanically strengthened new Hagi porcelain developed by controlling the chemical environment of iron

In order to enhance the mechanical strength of Hagi Porcelain (Hagiyaki), one of the oldest and famous potteries in Japan, new preparation condition was examined. Tempered Hagi porcelain, denominated as ‘Hagi Porcelain B’, was prepared with the Porcelain clay originating from Daido district, Yamaguchi Prefecture, Japan. Structural change of ‘Hagi Porcelain B’ was investigated by means of ⁵⁷Fe-Mössbauer spectroscopy, X-ray diffractometry (XRD) and three-point bending test. Mechanical strength of the ‘original Hagi Porcelain B’ was estimated to be 43.1 MPa by means of the three-point bending test, while much larger value of 104.5 MPa could be achieved when tempered by a chemical modification. Mössbauer spectrum of the ‘original Hagi porcelain B’ was composed of a paramagnetic doublet and a magnetic sextet due to Fe(III) of γ-Fe₂O₃(maghemite), while only one paramagnetic doublet due to to octahedral Fe(II)O₆ was observed for the ‘tempered Hagi Porcelain B’ with isomer shift and quadrupole splitting values of 1.13 and 2.15 mm s^?1, respectively. It is considered that the absence of magnetic phase causes an increase of the mechanical strength because the maghemite phase has a defect spinel structure. These results indicate that mechanical strength of the ‘Hagi porcelain B’ could be enhanced by controlling the sintering condition.     

Oxotitanium(IV) complexes of some bis‐unsymmetric Schiff bases: Synthesis,structural elucidation and biomedical applications

A number of oxotitanium(IV) complexes of the type TiOL with bis‐unsymmetric dibasic tetradentate Schiff base (LH₂) containing ONNO donor atoms have been synthesized. Mono‐Schiff base (OPD‐HNP) was prepared by the condensation of 1:3 molar ratio of 2‐hydroxy‐1‐naphthaldehyde (HNP) with o‐phenylenediamine (OPD). Dibasic unsymmetric tetradentate diamine Schiff bases were prepared by the reaction of OPD‐HNP with 2‐hydroxyacetophenone, 2‐hydroxypropeophenone, benzoylacetone, acetylacetone and ethylacetoacetate. Further, titanylacetylacetonate was reacted with these ligands to obtain their metal complexes. On the basis of analytical and physiochemical data, the formation of complexes as TiOL was suggested having square pyramidal geometry. Quantum mechanical approach also confirmed this geometry. The assessment of the synthesized ligands and their complexes showed that some behave as good inhibitors of mycelial growth against selected phytopathogic fungi but weak inhibitors against some selected bacteria. A few of them also showed antioxidant properties.     

Tentative Comparison of Tube Radial Distribution Chromatography and CZE

Tube radical distribution chromatography (TRDC) uses an untreated open tubular capillary tube and a ternary mixture of solvents (water and hydrophilic/hydrophobic organic solvents) as a carrier solution. A model analyte mixture comprising 1-naphthol, 1-naphthoic acid, 1-naphthalenesulfonic acid, 2,6-naphthalenedisulfonic acid, and 1,3,6-naphthalenetrisulfonic acid was examined by the TRDC and capillary zone electrophoresis (CZE) systems that comprised mainly a capillary tube and a detector. In the TRDC system the elution order of analytes could be changed by altering the component ratios of the solvents, whereas in the CZE system the elution order was changed by altering the electroosmotic flow direction. The experimental data obtained provide clues about the features and utility of TRDC as a new separation method.     

Complexation of acyclic ligands having two terminal quinoline units with alkali metal cations

Abstract

Acyclic multidentate ligands consisting of an oligooxyethylene chain (di-, tri-, tetra-, and penta-) and two terminal rigid quinaldate end groups were newly prepared and their complexation properties with alkali metal cations were estimated by the solvent extraction method to indicate a better affinity for K⁺. Among them, the tetraethylene glycol derivative showed the highest K⁺ binding on about the same level as 18-crown-6. Their conformations in solution and in the solid state were examined by using ¹H- and ¹³C-NMR spectroscopy and X-ray crystal analyses, respectively. The better binding of K⁺ in comparison with the corresponding glymes or analogues having the same donor sites was reasonably explained by considering the effective co-ordination of the carbonyl oxygen of the ester groups and the parallel π-stacking interaction between two quinaldate surfaces.     

How Strain Affects the Reactivity of Surface Metal Oxide Catalysts

Highly dispersed molybdenum oxide supported on mesoporous silica SBA‐15 has been prepared by anion exchange resulting in a series of catalysts with changing Mo densities (0.2–2.5 Mo atoms nm^?2). X‐ray absorption, UV/Vis, Raman, and IR spectroscopy indicate that doubly anchored tetrahedral dioxo MoO₄ units are the major surface species at all loadings. Higher reducibility at loadings close to the monolayer measured by temperature‐programmed reduction and a steep increase in the catalytic activity observed in metathesis of propene and oxidative dehydrogenation of propane at 8 % of Mo loading are attributed to frustration of Mo oxide surface species and lateral interactions. Based on DFT calculations, NEXAFS spectra at the O‐K‐edge at high Mo loadings are explained by distorted MoO₄ complexes. Limited availability of anchor silanol groups at high loadings forces the MoO₄ groups to form more strained configurations. The occurrence of strain is linked to the increase in reactivity.